NH3295H | TGIC | Filler & Pigment | Flow agent | Benzoin | 701 |
558 | 48 | 383 | 8 | 4 | 5 |
Appearance | White or light yellow transparent flakes |
Color (50% DMF) | max:3 |
Acid Number (mgKOH/g) | 41~45 |
Softening Point (℃) | 105~115 |
Glass Transition Temp. (℃) | ~69 |
Melting Viscosity (200℃, cone/plate, mPa·s) | 4400~5600 |
Reactivity at 180℃ (s, 8% TGIC) | 160~280 |
Curing Requirement | 200℃×10min |
Packaging | PE Bags, Net Weight 25kg ± 0.1kg / bag |
Extrusion Condition | Two-screw Extruder | ||
Zone I: 90~110℃ | Zone II: 110~120℃ | ||
Speed of Revolution | 500~1200rpm | ||
Fineness of Powder | <100μm | ||
Application Condition | Electrostatic Spraying With | 40~70KV | |
Coating Film Thickness | 50~70μm | ||
Degreased Cold-rolled Steel | 0.5mm | ||
Film Properties | Gel Time (180℃, sec) | 240~360 | |
Horizontal Flow (180℃, mm) | 25~30 | ||
Gloss (60°) | ≥85% | ||
Bending (φ1mm) | Pass | ||
Adhesive (1mm, grade) | 0 | ||
Pencil Hardness | ≥1H | ||
Impact (50cm) | Pass |