Pre-accelerated marine grade resin thixotropic Pre-mix resin fiberglass resin for FRP swimming pools marine boat slides bathtub
2597 marine resin is accelerated and thixotropic type of unsaturated polyester resin synthesized from phthalic acid and maleic anhydride and standard diols. Has been dissolved in styrene monomer, with moderate viscosity
and reactivity.
Liquid resin performance index
|
performance |
parameter |
unit |
standard test |
|
Appearance |
Light purple viscous liquid |
- | Visual inspection |
|
Acid value |
18-26 |
mgKOH/g |
GB/T 2895-2008 |
|
Solid content |
61-68 |
% |
GB/T 7193-2008 |
|
Viscosity25℃ |
0.26-0.44 |
pa.s | GB/T 7193-2008 |
| stability80℃ |
≥24 |
h | GB/T 7193-2008 |
|
Typical curing properties |
25 ° C water bath, 100g resin plus 2ml methyl ethyl ketone peroxide solution and 4ml cobalt isooctanoate solution |
- | - |
|
Gel time |
25-35 |
min |
GB/T 7193-2008 |
Resin Casting Properties (Typical)
|
performance |
parameter |
unit |
standard test |
|
Pasteurian hardness |
35-40 |
|
GB/T 3854 |
| Tensile Strength | 68 | Mpa |
GB/T 2567-2008 |
|
Tensile modulus of elasticity |
3500 |
Mpa |
GB/T 2567-2008 |
|
elongation at break |
3 |
% |
GB/T 2567-2008 |
|
bending strength |
100 |
MPa |
GB/T 2567-2008 |
|
Bending elastic modulus |
3500 |
MPa |
GB/T 2567-2008 |
|
Impact strength |
12 |
KJ/m2 |
GB/T 2567-2008 |
|
Heat distortion temperature |
60 |
℃ |
GB/T 1634-2004 |
|
Pasteurian hardness |
68 | - |
GB/T 3854-2005 |
|
Absorbability |
0.15 |
% |
GB/T 1034-2008 |
Practical example of business partner shows
Guangdong Good Resin Co., Ltd. is a well-known high-technology enterprise in south China, which is specialized in chemical composite materials research and development, production, sales, trade as one of the company. The main products are vinyl preservative resin, epoxy resin, unsaturated polyester resin (191 general glass fiber reinforced plastic, ship resin, auto parts resin, sanitary ware resin, mold resin, handicraft resin, imitation jade resin, high transparent resin, crystal resin,Paint resin, resin curing agent, resin accelerator, resin release agent, mold release agent, styrene, mold silicone and other composite materials, glassfiber mat, glassfiber cloth, glassfiber yarn and other resin reinforcement materials.
Material: metal barrel
Net weight: 220kg / barrel
Gross weight: 236kg/barrel
80 barrels(17.6 tons)for a 20'' container
delivery time:within 2-7 working days since payment confirmed.
transportation: sea/ Land
sample ship by international express
1. Q: Is your company a manufacturer?
A: Yes,we are. At the same time, we are also agent other brand's products.
2. Q: Does your company offer sample?
A: Yes, we usually offer 1kg for free sample but the shpping cost should be bear by buyer.
3. Q:What is your company's transportation form?
A: Samples generally ship by international express, a large number of commodies can be shipped by land or water.
4: Q: What is the quality and price of your product?
A: Our product have a good quality and stable performance, with a cheap price and high quality, there are a large number of market at home and abroad. Due to fluctuations of the resin prices and it's not stable, maybe you have to ask customer service or contact us with E-mail to get a quotation for the latest price. thanks for your understanding.
5. Q: What is your delivery time?
A: Usually within 2-7 working days after payment confirmed.
- Step 1Find your interested products by search keywords
- Step 2Contact the supplier by clicking ”Enquire” or “request meeting” button, otherwise, you also could consult our import consultant.
- Step 3After verifying your email, get response from suppliers or our trade manager will contact you as soon as possible
- Step 4Set up meeting with the Chinese supplier without language barrier
E glass fiberglass woven roving fiberglass cloth for boat and surfboard fiberglass cloth 400g 600g 800g
Hot selling high quality tensile cheap liquid molding silicone rubber for silicon molds making