AWS E308-16
DESCRIPTION:
a. E308-16 weld metal(19Cr-9Ni)is austenite structure,it has excellent mechanical properties and shows good resistance to intergranular corrosion.
b. It can be used for all position welding with excellent performance:
stable arc,small spatters,good appearance of weld.And also the welding electrode shows good heat-resistance character,not easy to turn red and gas porosity is not produced.
APPLICATION:
It can be used to weld corrosion-resistant 06Cr19Ni10 and 06Cr18Ni11Ti stainless steel structures with working temperature lower than 300 ℃
ATTENTION:
a.Before welding,the welding electrodes should be baked at the temperature from 300-350℃ for one hour.
b.Using stainless steel brush to clean the weld seam,in order to avoid scrap iron entering and affect its quality.
Chemical Composition of Deposited Metal: (%)
| C | Mn | Si | S | P | Cr | Ni |
|
|
---|
Standard |
≤0.08 | 0.5-2.5 |
≤0.9 |
≤0.03 | ≤0.04 | 18-21 | 9-11 |
|
|
Result | 0.052 | 0.86 | 0.65 | 0.01 | 0.02 | 19.30 | 10.05 |
|
|
Mechanical Properties of Deposited Metal
| Tensile Strength σb(Mpa) | Elongation δ5 (%) |
---|
Standard | ≥550 | ≥35 |
Result | 620 | 47 |
Recommended Current(AC or DC*)
Size(mm) | Φ2.5×350 | Φ3.2×350 | Φ4.0×400 |
---|
Flat Current(A) | 50-85 | 80-120 | 100-150 |
Vertical,Overhead Current(A) | 45-80 | 70-110 | 90-135 |