BAg30CuZnSn(30%Ag) Brazing Ring

STANDARD
ISO 17672 Standard: Ag 130
AWS A5.8 Standard:
COMPOSITION(w.%)
Ag: 29-31 | Cu: Remainder | Zn: 30-32 | Sn: 1.0-3.0 | Other: ≤0.15
PROPERTIES
Solidus (°C ): 665
Liquidus (°C ): 755
Solidus (°F ): 1229
Liquidus (°F ): 1391
Brazing Temperature (°C ): 785-805
Brazing Temperature (°F ): 1445-1513
Electrical Conductivity (%IACS): 18
Resistance (microhm-cm): 9.6
Elongation: 18%
Tensile Strength (MPa): 500
Density (g/cm^3): 8.81
MANUFACTURE CAPABILITIES
Wire Diameter Range (mm): Φ0.3-Φ2.0 (spool) / Φ2.0 and above (coil)
Rod Diameter and Length Range (mm): diameter: 1.0-6.0 / length: 1-1000
Strip Thickness and Width Range (mm): thickness: above 0.05 / width: 3-80
Other Forms: Ring
APPLICATIONS
Application: Used for the brazing of copper and copper alloys, as well as for copper and ferrous metals.
Characteristics: This alloy can sometimes be used as an alternative to HGW SILV 35, and its liquidus is 20°C lower than that of HGW SILV 35‘s.
STORAGE
The products shall be stored in its package with proper sealing. The warehouse where the brazing alloys are stored shall be dry and well-ventilated. Do not store the products with volatile and corrosive substances, such as acid and alkali.