HGW SILV 5 Brazing Rod

STANDARD
ISO 17672 Standard: CuP 281
AWS A5.8 Standard: BCuP-3
COMPOSITION(w.%)
Ag: 4.8-5.2 | Cu: Remainder | P: 5.8-6.2 | Other: ≤0.25
PROPERTIES
Solidus (°C ): 645
Liquidus (°C ): 815
Solidus (°F ): 1193
Liquidus (°F ): 1499
Brazing Temperature (°C ): 845-865
Brazing Temperature (°F ): 1553-1624
Electrical Conductivity (%IACS): 9.6
Resistance (microhm-cm): 18
Elongation: 8%
Tensile Strength (MPa): 650
Density (g/cm^3): 8.14
MANUFACTURE CAPABILITIES
Wire Diameter Range (mm): Φ0.8-Φ2.0 (spool) / Φ2.0 and above (coil)
Rod Diameter and Length Range (mm): diameter: 1.0-4.0 / length: 1-1000
Strip Thickness and Width Range (mm): thickness: above 0.2 / width: 3-80
Other Forms: Ring
APPLICATIONS
Application: Used for the brazing of copper and copper alloys.
Characteristics: Recommended gap width is in the range of 0.06-0.13mm.
STORAGE
The products shall be stored in its package with proper sealing. The warehouse where the brazing alloys are stored shall be dry and well-ventilated. Do not store the products with volatile and corrosive substances, such as acid and alkali.