HGW SILV 0P7 Brazing Rod

STANDARD
ISO 17672 Standard: CuP 181;
AWS A5.8 Standard: BCuP-2
COMPOSITION(w.%)
Cu: Remainder | P: 7.2-7.5 | Other: ≤0.25
PROPERTIES
Solidus (°C ): 710
Liquidus (°C ): 793
Solidus (°F ): 1310
Liquidus (°F ): 1459.4
Brazing Temperature (°C ): 823-843
Brazing Temperature (°F ): 1513-1581
Electrical Conductivity (%IACS): 9.9
Resistance (microhm-cm): 17.4
Elongation: 3%
Tensile Strength (MPa): 500
Density (g/cm^3): 7.86
MANUFACTURE CAPABILITIES
Wire Diameter Range (mm): Φ0.5-Φ2.0 (spool) / Φ2.0 and above (coil)
Rod Diameter and Length Range (mm): diameter: 1.0-6.0 / length: 1-1000
Strip Thickness and Width Range (mm): thickness: above 0.3 / width: 3-80
Other Forms: Ring
APPLICATIONS
Application: Used for the brazing of copper and copper alloys.
Characteristics: This alloy has good fluidity. It is suited for the brazing of narrow gaps within the 0.025-0.076mm range.
STORAGE
The products shall be stored in its package with proper sealing. The warehouse where the brazingalloys are stored shall be dry and well-ventilated. Do not store the products with volatile and corrosive substances, such as acid and alkali.