HGW SILV 30 Flux-Cored Brazing Rod

STANDARD
ISO 17672 Standard: Ag 230
AWS A5.8 Standard: BAg-20
COMPOSITION(w.%)
Ag: 29-31 | Cu: 37-39 | Zn: Remainder | Other: ≤0.15
PROPERTIES
Solidus (°C ): 680
Liquidus (°C ): 765
Solidus (°F ): 1256
Liquidus (°F ): 1409
Brazing Temperature (°C ): 795-815
Brazing Temperature (°F ): 1463-1531
Electrical Conductivity (%IACS): 24.4
Resistance (microhm-cm): 7.1
Elongation: 9%
Tensile Strength (MPa): 560
Density (g/cm^3): 8.67
MANUFACTURE CAPABILITIES
Wire Diameter Range (mm): Φ0.3-Φ2.0 (spool) / Φ2.0 and above (coil)
Rod Diameter and Length Range (mm): diameter: 1.0-6.0 / length: 1-1000
Strip Thickness and Width Range (mm): thickness: above 0.05 / width: 3-80
Other Forms: Ring
APPLICATIONS
Application: Used for the brazing of copper and copper alloys, as well as for copper and ferrous metals.
Characteristics: This alloy has small crystal spacing. It has good fluidity and wettability.
STORAGE
The products shall be stored in its package with proper sealing. The warehouse where the brazing alloys are stored shall be dry and well-ventilated. Do not store the products with volatile and corrosive substances, such as acid and alkali.